Radiation-curable compositions for pigmented inks

ABSTRACT

The present invention relates to radiation-curable compositions useful as ink vehicles or inks, in particular UV-curable inks, such as UV-litho inks, comprising a (meth)acrylated styrene allyl alcohol copolymer obtained from the (meth)acrylation of a styrene allyl alcohol (SAA) copolymer with (meth)acrylic acid and/or one or more alkyl(meth)acrylates, and at least one alkoxylated acrylated monomer.

The present invention relates to radiation-curable compositions useful as ink vehicles or inks, in particular UV-curable inks, such as UV-litho inks.

UV-litho inks based on fatty acid modified polyester acrylate have been used since the 70ies with increasing success. Compared to conventional ink systems UV-inks exhibit faster curing versus oxidative drying and provide an easier printing process because of no drying on the rollers, which leads to short start-up times and less waste. However, fatty acid modified polyester acrylate-based inks still show several performance shortcomings compared to conventional ink systems like the ink-water balance (lack of ink-water emulsion stability on press), pigment wetting (lack of flow in ink duct), higher tack (picking) and higher misting, especially at higher press speeds.

A process for coating articles wherein a polymerizable prepolymer blend of an unsaturated ester of a vinyl aromatic hydrocarbon unsaturated alcohol copolymer such as styrene/allyl alcohol copolymer and a polymerizable interpolymer ester such as an unsaturated ester of a styrene/hydroxyalkyl acrylate/alkyl acrylate terpolymer is applied to the surface of the article to be coated and the prepolymer blend polymerized to form the coating using ionizing radiation is disclosed in U.S. Pat. No. 3,546,002.

U.S. Pat. No. 4,045,516 describes styrene-allyl alcohol copolymer-based solid polyene compositions which when mixed with liquid polythiols can form solid curable polyene-polythiol systems. These solid polyenes, containing at least two reactive carbon-to-carbon unsaturated bonds, are urethane or ester derivatives of styrene-allyl alcohol copolymers.

French patent number 2.168.623 discloses styrene allyl alcohol copolymer-based urethane acrylates. The allylic hydroxyls are reacted with diisocyanate and capped with hydroxy acrylates.

JP 49-94788 discloses the synthesis of styrene allyl alcohol (SAA) acrylates diluted in trimethylolpropane trimethacrylate (TMPTA) as UV vehicles for printing inks.

While the known UV-litho inks exhibit good performance in some of their parameters, there is still a need for further ink vehicles and inks having improved properties such as an improved water balance, an improved pigment wetting and/or an improved cure speed. The subject inventors have now surprisingly found that if (meth)acrylated SAA copolymer-based radiation-curable ink vehicles or inks are diluted with an alkoxylated (meth)acrylated monomer instead of a (meth)acrylated monomer such as TMPTA, water balance, pigment wetting and/or cure speed of the obtained ink vehicle or ink are improved.

Therefore, the present invention relates to a radiation-curable composition comprising (a) at least one (meth)acrylated styrene allyl alcohol copolymer resulting from the reaction of a styrene allyl alcohol copolymer (SAA) with (met)acrylic acid and/or one or more alkyl(meth)acrylates, and (b) at least one alkoxylated (met)acrylated monomer.

SAA copolymers are known in the art. By SAA copolymers it is intended to designate copolymers having units derived from allyl alcohol and units derived from styrene. SAA copolymers are for example produced by Lyondell via a radical polymerization of styrene and allyl alcohol as shown in the following scheme:

A process for making allylic/alkylenic copolymers is for example disclosed in WO 99/62969.

SAA copolymers are commercially available from Lyondell in three grades, SAA-100, SAA-101 and SAA-103. The properties of these copolymers which are preferred for the preparation of the present compositions are summarized in the following table 1. TABLE 1 SAA-100 SAA-101 SAA-103 Composition Styrene mole % 70 60 80 Allyl alcohol mole % 30 40 20 Physical properties Physical form Pastilles Pastilles Pastilles color, Apha(30% in MEK) 40 40 40 Mn, GPC 1500 1200 3200 Mw, GPC 3000 2500 8400 Pd 2 2.1 2.6 OH number, mg KOH/g 210 255 125 Acid number, mg KOH/g <0.1 <0.1 <0.1 Tg, ° C. 62 57 78 Softening point, ° C. 79 73 90

The hydroxyl groups of the SAA copolymers are stable to acids and bases and easily converted to (meth)acrylate by direct esterification with (meth)acrylic acid or by transesterification with an alkyl(meth)acrylate. The SAA copolymer can for example be dissolved in toluene and then reacted with acrylic acid or methacrylic acid under known process parameters as exemplified in the following scheme:

For the purpose of the present invention all acrylated copolymers and monomers may be derived from acrylic acid, methacrylic acid and from alkylacrylates and alkylmethacrylates. For reasons of simplicity these compounds are uniformly called “(meth)acrylated”, but it is to be understood that (meth)acrylated copolymers and monomers encompass acrylated and methacrylated copolymers and monomers throughout the present description and claims.

For reasons of processability and handling, SAA copolymer (meth)acrylates are preferably produced in the presence of a diluent. This diluent can be added during (polyol or (meth)acrylated polyol) or after the (meth)acrylation step (only (meth)acrylated polyol). It has been found that alkoxylated (meth)acrylated monomers are particularly suitable as diluents for (meth)acrylated SAA copolymers. Moreover, litho inks based on (meth)acrylated SAA copolymers according to the invention with alkoxylated (meth)acrylated monomers as diluents show exceptional performance compared to state of the art UV inks for water balance and pigment wetting. Additionally, depending on the alkoxylated (meth)acrylated monomer a composition exhibiting a very high cure speed can be obtained.

Besides the SAA and the diluent, other components such as an acidic component, preferably a fatty acid, can be added during the synthesis to modify the properties. The quantity of fatty acid added is generally from 0 to 50% by weight based on the total weight of copolymer and monomer.

The (meth)acrylated styrene allyl alcohol copolymers used in the composition according to the invention is preferably obtained from the reaction of a styrene allyl alcohol copolymer (SAA) with acrylic acid. Most prefered is a acrylated styrene allyl alcohol copolymer obtained from the acrylation of a styrene allyl alcohol copolymer with acrylic acid in the presence of an alkoxylated polyol so that both the styrene allyl alcohol copolymer and the alkoxylated polyol are acrylated simultanously.

A monomer is herein defined as a component able to be further polymerized. It can be di- or tri-functional but also tetra, penta or even hexafunctional.

Generally, the composition of the present invention should comprise the minimum amount of 10% by weight, more preferably a minimum amount of 40% by weight and most preferably a minimum amount of 50% by weight alkoxylated (meth)acrylated monomer, based on the total weight of the (meth)acrylated SAA copolymer and the monomer. For example the composition may comprise 10-90% by weight (meth)acrylated SAA copolymer and 10-90% by weight alkoxylated (meth)acrylated monomer, preferably 40-70% by weight (meth)acrylated SAA copolymer and 30-60% by weight alkoxylated (meth)acrylated monomer, each based on the total weight of copolymer and monomer.

The alkoxylated (meth)acrylated monomer used in the compositions of the present invention are those currently used in radiation-curable compositions. They can for example be obtained from mono-, di-, tri- and polyhydroxy compounds being alkoxylated and (meth)acrylated. The preferred alkoxylates are ethoxylates and propoxylates or mixtures thereof. Each of the hydroxy groups of the hydroxy compounds may bear one or more, preferably at least 2, alkoxy repeating units. The number of alkoxy repeating units on each hydroxy group generally does not exceed 10, preferably not 5.

Advantageously, the alkoxylated (meth)acrylated monomer used in the composition of the present invention is selected from the group consisting of alkoxylated triol tri(meth)acrylates, alkoxylated diol di(meth)acrylates, and more particularly alkoxylated (meth)acrylated bisphenol A derivatives. Preferably, the alkoxylated (meth)acrylated monomer is chosen from ethoxylated glycerol tri(meth)acrylates, propoxylated glycerol tri(meth)acrylates, ethoxylated neopentylglycol di(meth)acrylates, propoxylated neopentylglycol di(meth)acrylates, ethoxylated trimethylolpropane tri(meth)acrylates, propoxylated trimethylolpropane tri(meth)acrylates, (meth)acrylated bisphenol A ethoxylates, (meth)acrylated bisphenol A propoxylates, alkoxylated ditrimethylolpropane tetra(meth)acrylates, alkoxylated pentaerythritol tetra(meth)acrylates, alkoxylated dipentaerythritol penta/hexa (meth)acrylates. Particularly preferred monomer diluents are (meth)acrylated bisphenol A alkoxylates such as acrylated bisphenol A ethoxylate, available as Ebecryl™ 150 from Surface Specialties-UCB. Propoxylated glycerol triacrylate is for example available under the trademark OTA480.

The radiation-curable composition of the present invention is useful as ink vehicle for the preparation of inks, such as UV-litho inks. Therefore, the composition may further comprise one or more compounds selected from pigments, photoinitiators, and ink additives.

The pigments used in the compositions of the invention are those pigments generally used in paste or liquid inks. A list of such pigments can be found in the Color Index. More particularly, those pigments may be cited such as Process Yellow 13 (Diarylide Yellow-Irgalite BAW of Ciba, Permanent GR of Clariant), Process Magenta Pigment 57 (Bona Calcium-Ilobona 4BY of Sun, Irgalite SMA of Ciba), Process Blue 15.3 (Copper Phthalocyanine-Irgalite GLO of Ciba, Hostaperm Blue B2G of Clariant), Process Black 7 (Oxidised Carbon Black-Special Black 250; Special Black 350 of Degussa), etc. The pigments are preferably used at 1-50% by weight of the total weight of the composition, more preferably at 1-40% by weight.

The photoinitiators usable in the compositions of the invention are well known in the art. They can be chosen from α-hydroxyketones, α-aminoketones, benzildimethyl-ketals, acyl phosphines, benzophenone derivatives, thioxanthones and blends of these. They are used at 0 to 15% by weight. Photoactivators are generally chosen between amine derivatives. The photoinitiators need only be used if the compositions are cured by ultraviolet light. The compositions may also be cured by electron beams rays, and, in this case, no photoinitiator needs to be added to the composition.

The additives are those commonly used in inks, such as stabilizers, substrate wetting agents, anti-foam agents, adhesion promoters, dispersing agents etc.

Preferably, the composition of the present invention comprises a minimum amount of 40% by weight, more preferably a minimum amount of 50% by weight, of (meth)acrylated SAA copolymer and alkoxylated (meth)acrylated monomer, based on the total weight of the composition.

The compositions of the present invention may comprise each one (meth)acrylated SAA copolymer and one alkoxylated (meth)acrylated monomer or, if desired, two or more different (meth)acrylated SAA copolymers and two or more different alkoxylated (meth)acrylated monomers.

The compositions of the present invention can be prepared by (meth)acrylating SAA copolymer as described above by (meth)acrylating the SAA copolymer with (meth)acrylic acid or with an alkyl(meth)acrylate, in the presence of a solvent. Work-up of the reaction product is, however, difficult due to the high viscosity of the (meth)acrylate. To ensure efficient washes and phasing of the (meth)acrylated SAA copolymer, a diluent in the form of the alkoxylated (meth)acrylated monomer can be added directly after (meth)acrylation, but before the solvent removal ((meth)acrylation of SAA with post dilution with (meth)acrylated polyols or “post dilution process”).

In a variant, the SAA can be (meth)acrylated in presence of (meth)acrylated polyols.

It has now surprisingly been found that if the SAA copolymer and the diluent in the form of an alkoxylated polyol monomer are (meth)acrylated simultaneously in-situ (co-acrylation process) better properties can be obtained such as ink water balance. The positive impact on monomer hydroxyl conversion of the co-acrylation process compared to the post dilution process is demonstrated by the LCMS data summarized in the following table 2: Monomer composition Diluent (LC area %) Resin Process SAA Type % Mono Di Tri 1 Co-acrylation 103 OTA480 50 0.8 5.4 93.8 2 Post-dilution 103 OTA480 50 1.2 10.4 88.4 3 Co-acrylation 100 Eb150 60 7 93 NA 4 Post-dilution 100 Eb150 60 14 86 NA 5 Co-acrylation 103 Eb150 70 5 95 NA 6 Post-dilution 103 Eb150 70 12 88 NA

The above table shows that bisphenol A ethoxylate (Ebecryl™ 150) is less monoacrylated and propoxylated glycerol (OTA480) is less mono- and diacrylated (based on LC % area) in the co-acrylation process compared to the post dilution process. While applicant does not wish to be bound to any theory, it is believed that this effect can probably explain the improvement in the ink-water balance of compositions prepared according to the co-acrylation process compared to the compositions prepared according to the post dilution process.

Remarkably, there is also a difference in appearance when the co-acrylation process is used. The obtained resin is much less colored.

Furthermore, the cure speed of the compositions of the present invention has been measured in a cyan ink with 8% photoinitiator blend (32% EDB/13% DETX/7% Irgacure369/14% benzophenone/34% BDK) under a 120 Wcm Hg lamp by graphite test. The results are summarized in the following table 2a: Cure speed SAA Process Diluent Alkoxylation m/min 100 co-acrylation EB150:65% OE 100 100 post dilution EB150:60% OE 90 100 co-acrylation EB150:60% OE 90 100 co-acrylation OTA480:45% OP 40 100 co-acrylation BisA(OP)2DA OP 70 100 co-acrylation BisA(OP)4DA OP 60 100 co-acrylation TMP(EO)3TA OE 25 103 co-acrylation EB150:70% OE 110 103 post dilution EB150:70% OE 90 103 post dilution OTA480:50% OP 20

It can be seen from the above table 2a that the cure speed is not significantly influenced by the process used (co-acrylation or post dilution). Surprisingly, cure speed of Bisphenol A monomers is greater than for other monomers such as OTA 480 or alkoxylated TMPTA. Among the Bisphenol A monomers, ethoxylated Bisphenol A monomers have a higher cure speed and are thus preferred over propoxylated Bisphenol A monomers.

Inks are generally made in 2 steps, the pigment dispersion step and the letdown step. In the 1st step, all the pigments are added in the pigment dispersing binders (oligomers and monomers). They are mixed and then dispersed on a triple roll or bead mill. A few passes are necessary to achieve a good dispersion. Pigments that are difficult to disperse require more number of passes. It is the same with the binders. Binders that are not good for pigment wetting also require additional passes. Once the pigment has achieved this fineness, the pigment paste is diluted with the letdown. The letdown has to be compatible with the binder used to disperse the pigments. The finished ink is then printed onto the substrate. The ink film is then cured under a UV lamp, for example at 120 W/cm and 30 m/min. A few passes may be required to cure the ink if the binder is not reactive enough.

The invention also relates to the polymeric compositions obtainable by curing the radiation curable composition as well as to substrates being partially or entirely coated with the polymeric composition.

Pigment wetting can be evaluated by different methods:

-   -   Rheology: Pigment wetting is a major factor of influence on the         rheology. Inks with bad wetting of the pigment are showing a         marked shear thinning effect, whereby the viscosity is high at         low shear rate and drops as the shear rate is increased. This         results in a high shortness index (SI=ratio of low shear         viscosity to high shear viscosity. For liquid inks a Newtonian         rheology is required. Ideally, this means that the viscosity is         independent of the shear rate. (SI=1). Paste inks are more         pseudoplastic, showing a shear depending viscosity. (SI>1). Too         high SI (too high low shear viscosity) may result in bad flow in         the ink duct.     -   The rheology is measured with cone and plate type rheometers.     -   Optical density: Pigment wetting can also be evaluated by         measuring the color density of the printed ink at constant film         thickness. In this case the ink is printed using a lab         applicator and the color density is measured with a         densitometer, which spectrophotometrically compares the         reflected light to the incident light.

For the present invention the pigment wetting is rated on a scale from 5=excellent to 0=bad pigment wetting.

The water balance of the compositions of the present invention was evaluated on lithotronic. Basically, the Lithotronic measures the torque needed for a certain speed (rpm). The torque gives a measure for viscosity. With the Lithotronic, the change in viscosity of an ink is measured when water is emulsified in it.

The measurement consists of two phases: preconditioning and measurement.

During preconditioning, the sample is sheared at constant speed and heated at the same time to a certain preprogramed temperature. At the end of the preconditioning phase, the sample has reached a stable viscosity. At that moment, controlled metering of fount solution is started. Changes of applied torque (hence viscosity) versus time and emulsion capacity are recorded. When maximum emulsion capacity is reached, a drop in torque is usualy experienced because of the free water in the beaker.

At first contact with water, change of torque (delta T) should be small. Further, when water is emulsified in the ink, viscosity should only undergo a minor increase. This ensures a good ink transfer on the press. If the emulsion is too fine and too stable (too high increase of viscosity), it will lead to a loss of density and possible ink build up. If the emulsion is too coarse (viscosity decrease), it can lead to unstable press behaviour making regular press control necessary.

For the present invention the ink water balance is rated by the type of emulsion (F=good ink water balance characterized by a limited viscosity increase, resulting from a fine emulsion; C=bad ink water balance characterized by a high viscosity decrease, resulting from a coarse emulsion).

The invention will now be illustrated by the following non-limiting examples and tests which are by way of illustration only. Unless otherwise indicated, herein all the test results and properties herein were performed using conventional methods well known to those skilled in the art. The amounts in the tables are given in % by weight based on the total weight of the composition.

The compositions of the present invention were prepared according to the following production examples:

Composition 1

A reactor was charged with 524 grams of SAA-100 from Lyondell (1.96 eq), 921.4 grams Simulsol BPJE (ethoxylated bisphenol A from Seppic-Air Liquide) (4.60 eq), 496.4 grams acrylic acid (6.89 eq), 1295 grams toluene, 48.5 grams para-toluenesulphonic acid, 0.50 grams Cu₂O, 9.7 grams hypophosphorous acid. The reactor content was heated at 120° C. until the rate of reaction slows down as measured by collection of the esterification water. After about 8 to 10 hrs when the acid value was less than 15, the reactor was cooled down to 50° C. and diluted with toluene till a 1/1 reactant:solvent ratio. The reactor was charged with an aqueous solution of 15% sodium chloride and stirred for 2 minutes. Phases were let to separate at 40-50° C. and the aqueous phase decanted. Ssaline washes were repeated until an acid value of 5 was reached. The reactor was charged with a caustic solution of 5% NaOH in an amount of 25% of the batch weight and stirred for 2 minutes. Phases were separated at 40° C. and the aqueous layer was decanted. Then 1.8 grams HQ and 3.6 grams trisnonylphenylphosphite were added and heated till 120° C. to distill the remaining water. An airsparge of 1 l/hr was maintained. When the water content was below 0.1% the reactor was cooled down for filtration. After distillation of the toluene at 90° C. and a reduced pressure of 30 mbar, a product A1 with a Cone & Plate viscosity of 33 Pas and an acid value of 0.7 mg KOH/g was obtained.

Composition 2

A reactor was charged with 399.9 grams of SAA-103 from Lyondell (0.90 eq), 65.0 grams acrylic acid (0.90 eq), 313 grams toluene, 11.8 grams para-toluenesulphonic acid, 0.07 grams Cu₂O, 2.35 grams hypophosphorous acid. The reactor content was heated at 120° C. until the rate of reaction slowed down as measured by collection of the esterification water. After about 8 to 10 hrs when the acid value was less than 15, it was cooled down to 50° C. and diluted with toluene till a 1/1 reactant:solvent ratio. The reactor was charged with an aqueous solution of 15% sodium chloride and stirred for 2 minutes. Phases were let to separate at 40-50° C. and the aqueous phase decanted. Saline washes were repeated until an acid value of 5 was reached. The reactor was charged with a caustic solution of 5% NaOH in an amount of 25% of the batch weight and stirred for 2 minutes. Phases were separatde at 40° C. and the aqueous layer decanted. Then, 1050 grams acrylated bisphenol ethoxylate (EB 150 from Surface Specialties—UCB), 1.5 grams HQ and 3.0 grams trisnonylphenylphosphite were added and heated till 120° C. to distill the remaining water. An airsparge of 1 l/hr was maintained. When the water content was below 0.1% the reactor was cooled down for filtration. After distillation of the toluene at 90° C. and a reduced pressure of 30 mbar, a product B1 with a Cone & Plate viscosity of 53 Pas and an acid value of 1.05 mg KOH/g was obtained.

Further compositions were prepared according to the above production examples. The following compositions (products A1-A5 and B1-B2) were obtained according to the invention: TABLE 3 Viscosity Acid Pas; value SAA Diluent 25° C. Mg Example copolymer Type level C&P KOH/g Product A1 SAA 100 Bis A (EO)4 DA 65% 33 0.7 Product A2 SAA 100 Bis A (PO)2 DA 80% 75 0.8 Product A3 SAA 100 Bis A (PO)4 DA 75% 130 0.8 Product A4 SAA 100 TMP (EO)3 TA 45% 40 1.2 Product A5 SAA 100 Glycerol (PO)3 45% 87 0.8 TA Product B1 SAA 103 Bis A (EO)4 DA 70% 53 1.05 Product B2 SAA 103 Glycerol (PO)3 50% 117 0.8 TA

In the above table 3 the following abbreviations are used:

-   -   Bis A: bisphenol A     -   TMP: trimethylolpropane     -   EO: ethyleneoxide     -   PO: propyleneoxide     -   DA: diacrylate     -   TA: triacrylate     -   C&P: Cone and Plate

The following comparative compositions were prepared as well: TABLE 4 Viscosity Pas; Diluent 25° C. Acid value Example Polymer Type level C&P Mg KOH/g Product C1 SAA 100 TMPTA 50% 33 0.9 Product C2 SAA 100 HDDA 30% 75 0.9 130 Product C3 PEA:Eb657 NA NA 40 <15 Product C4 PEA:Eb811 NA NA 87 <1

In the above table 4 the following abbreviations are used:

-   -   PFA:Eb657: Polyester acrylate Ebecryl™ 657     -   PEA:Eb811: Polyester acrylate Ebecryl™ 811     -   TMPTA: trimethylolpropane trimethacrylate     -   HDDA: Hexane diol diacrylate     -   NA: not applicable.

With the above compositions and comparative compositions the following ink formulations were prepared: TABLE 5 A1 A2 A3 A4 A5 B1 B2 C1 C2 C3 C4 Oligomer 64 50 62 59 60 58 58 64 66 57 60 Stab 1 1 1 1 1 1 1 1 1 1 1 PB 15:3 17 17 17 17 17 17 17 17 17 17 17 Talc 6 6 6 6 6 6 6 6 6 6 6 PI blend 8 8 8 8 8 8 8 8 8 8 8 OTA480 8 10 11 8 TMPTA 4 HDDA 2 TMP(EO)3TA 9 Ebecryl ™ 150 4 10 BPA(OP)2DA 18 BPA(OP)4DA 6 Stab: polymerisation inhibitor (5% solution of NPAL in DPGDA (DiPropyleneGlycolDiAcrylate); NPAL = Tris(N-nitroso-N-phenylhydroxylamine)aluminium salt) PB15:3 = phtalocyanine pigment (Irgalite ™ GLO from Ciba)

Various properties of the obtained ink formulations were measured. The results are summarized in the following table 6: TABLE 6 A1 A2 A3 A4 A5 B1 B2 C1 C2 C3 C4 Visco 2.5 s-1 62.2 61.5 63.0 75.0 73.1 58.1 76.8 71.2 131 72.0 71.0 Visco 100 s-1 35.1 34.8 33.1 34.5 34 32.5 34.3 30.4 37.6 30.0 30.2 SI 1.8 1.8 1.9 2.2 2.1 1.8 2.2 2.3 3.5 2.4 2.4 Optical Density 2.05 1.99 2.08 1.98 2.08 2.08 2.13 2.1 1.7 1.95 2.04 Pigment wetting 4 4 4 3 3 4 3 2 1 2 2 Delta T 9 8 8 9 12 9 8 9 5 23 20 Emulsion F F F F F F F C C C C Cure speed 100 70 60 25 40 110 30 40 50 20 20 Cure speed: m/min at 120 W/cm (graphite test)

Furthermore, a comparison between product A1 of the present invention and an ink formulation based on polyesteracrylate (Ebecryl657) was conducted with various pigments. The ink formulations prepared are summarized in the following table 7: TABLE 7 Black Cyan Magenta Yellow A1 Eb657 A1 Eb657 A1 Eb657 A1 Eb657 Oligomer 63.5 59 64 57 64 59 68 64 Stab 1 1 1 1 1 1 1 1 P. Black 7 20 20 P. Blue 15:3 17 17 P. Red 57:1 18 18 P. Yellow 13 14 14 P. Blue 61:1 1.5 1.5 Talc 6 6 3 3 3 3 PI blend 8 8 8 8 8 8 8 8 OTA480 10.5 11 11 10 Eb150 6 4 6 6

Various parameters of the obtained inks were measured. The results are summarized in the following table 8: TABLE 8 Black Cyan Magenta Yellow A1 Eb657 A1 Eb657 A1 Eb657 A1 Eb657 Visc. 2.5 s-1 55.9 102 62.2 72.0 40.3 60.1 97.4 87 Visc. 100 s-1 32.1 31.7 35.1 30.0 33.9 33.4 34.8 34.8 SI 1.7 3.2 1.8 2.4 1.2 1.8 2.8 2.5 Optical density 2.35 1.59 2.05 1.95 1.8 1.84 1.65 1.60 Pigment wetting 4 0 4 2 5 3 2 2 Delta T (%) 9 19 9 23 6 10 7 20 Emulsion F C F C F/C C F C Cure speed 70 30 100 20 80 30 70 20 Cure speed: m/min at 120 W/cm (graphite test)

The above results demonstrate that the compositions of the present invention exhibit an improved water balance and an improved pigment wetting compared to acrylated SAA copolymer-based ink vehicles which do not comprise an alkoxylated acrylated monomer and an improved water balance and an improved pigment wetting compared to polyester acrylate ink vehicles. Moreover, the cure speed of the radiation-curable composition according to the present invention can be higher compared to the known compositions depending on the alkoxylated acrylated monomer employed. 

1. Radiation-curable composition, comprising (a) at least one (meth)acrylated styrene allyl alcohol copolymer obtained from the (meth)acrylation of a styrene allyl alcohol (SAA) copolymer with (meth)acrylic acid and/or one or more alkyl(meth)acrylates, and (b) at least one alkoxylated acrylated monomer.
 2. Composition according to claim 1, comprising 10-90% by weight (meth)acrylated SAA copolymer and 10-90% by weight alkoxylated (meth)acrylated monomer, each based on the total weight of the (meth)acrylated SAA copolymer and alkoxylated (meth)acrylated monomer.
 3. Composition according to claim 1, wherein the alkoxylated (meth)acrylated monomer is selected from the group consisting of alkoxylated triol tri(meth)acrylates, alkoxylated diol di(meth)acrylates, preferably alkoxylated (meth)acrylated bisphenol A derivatives, more preferably oxyethylated.
 4. Composition according to claim 3, wherein the alkoxylated (meth)acrylated monomer is selected from the group consisting of ethoxylated glycerol tri(meth)acrylates, propoxylated glycerol tri(meth)acrylates, ethoxylated neopentylglycol di(meth)acrylates, propoxylated neopentylglycol di(meth)acrylates, ethoxylated trimethylolpropane tri(meth)acrylates, propoxylated trimethylolpropane tri(meth)acrylates, (meth)acrylated bisphenol A ethoxylates, (meth)acrylated bisphenol A propoxylates, alkoxylated ditrimethylolpropane tetra(meth)acrylates, alkoxylated pentaerythritol tetra(meth)acrylates and alkoxylated dipentaerythritol penta/hexa (meth)acrylates.
 5. Composition according to claim 1, further comprising one or more compounds selected from pigments, photoinitiators, and ink additives, such as stabilizers, substrate wetting agents, anti-foam agents, adhesion promoters, dispersing agents etc.
 6. Process of preparing a radiation-curable composition, comprising the steps of a) admixing a styrene allyl alcohol (SAA) copolymer with at least one alkoxylated polyol and b) in-situ (meth)acrylating the mixture obtained under a).
 7. Radiation-curable composition obtainable by the process of claim
 6. 8. Vehicle or ink containing the radiation-curable composition as claimed in claim
 1. 9. Polymeric composition obtainable by curing the radiation-curable composition as claimed in claim
 1. 10. Substrate partially or entirely coated with the polymeric composition as claimed in claim
 9. 